Feasibility of orbital friction stir welding on clad pipes of API X65 steel and Inconel 625

Scientific Reports volume 13, Article number: 10669 (2023) Cite this article

526 Accesses

1 Citations

Metrics details

An Author Correction to this article was published on 24 July 2023

This article has been updated

Orbital friction stir welding (FSW) has been applied to clad pipes, which is certainly of interest to the oil and gas industry. In this context, an FSW system capable of performing sound joints in one pass with full tool penetration was developed. Orbital FSW was executed in 6 mm thick API X65 PSL2 steel clad pipes with 3 mm thick Inconel 625 using a polycrystalline cubic boron nitride (pcBN) tool. The metallurgical and mechanical properties of the joints were investigated. Sound joints with axial forces of 45–50 kN, tool rotational speeds of 400–500 rpm, and a welding speed of 2 mm/s were obtained, illustrating that the developed system can perform FSW joints without volumetric defects.

The main challenges of the oil and gas industry are related to the exploration of deep and ultra-deep wells, which present an aggressive environment with salt and gasses like H2S and CO2. In this context, the usage of carbon steel pipes clad in a corrosion resistant alloy (CRA) has proven to be a suitable option to meet design requirements at low manufacturing costs1,2,3. However, pipeline welding currently used by the oil and gas industry, such as fusion-based welding, often involves high temperatures and can cause metallurgical issues owing to dissimilar joints (e.g., clad pipes), thus resulting in solidification cracking, hard microstructures at the interface, high tensile residual stresses and excessive carbon diffusion that may compromise the joint performance4,5.

Orbital friction stir welding (FSW), a solid-state joining process, is recognized as a suitable alternative that has the potential to minimize the challenges typically found in fusion-based welding since it is performed at lower temperature and shorter processing time, which results in reduced energy input, avoiding (or minimizing) most of the above-mentioned issues6,7. FSW uses the friction energy produced between the materials to be joined and a non-consumable rotating tool. Two approaches are used in orbital FSW: in the first, the pipe rotates while the rotating tool remains stationary; and in the second, the entire tool head rotates while the pipe remains stationary8. As for the classical FSW, severe plastic deformation and material flow occur along the welding path. In short, the material is transported from the front of the tool to the trailing edge, later forged, producing the joint9,10,11.

Although FSW is successfully applied to sheets of various materials, orbital FSW involves challenges to be overcome since there are difficulties associated with the clamping device8,12. Challenges of FSW to complex and circular-shaped joints were recently reviewed by Senthil et al.8, where the clamping system was one of the most significant factors for the welding process itself. For instance, due to the high forces during FSW, internal support of the pipes is required. Another difference when welding pipes is the contact of the tool with the parts to be joined, e.g., depending on the diameter of the pipe, the curvature of the pipe results in a non-complete contact of the tool shoulder with the workpiece, thus influencing the material flow and heat generation12,13. Senthil et al.8 also pointed out that before FSW can be considered for industrial pipe joining, a deep understanding of the influence of the clamping system is essential.

Overall, only a few studies were performed on orbital FSW on pipeline steels using different approaches to achieve sound joints. Feng et al.14 studied orbital FSW welding of an API X65 steel, where sound welds were obtained using a specially designed portable FSW system. The joints showed slightly higher mechanical strength and superior impact resistance than the base material (BM). Giorjao et al.15 performed orbital FSW in an 8 mm thick super duplex stainless steel pipe in force control mode and total tool penetration. Hardness and tensile tests showed a hardness increase in the stir zone (SZ) and failure on the BM. However, orbital FSW in clad pipes is scarce, but surely needed for industrial application.

In this work, orbital FSW on clad pipes of API X65 steel and alloy 625 was performed. A very rigid clamping system to handle the forces and torque during the process was employed to enable orbital FSW, ensuring a constant weld quality for the pipes. Thus, one pass orbital FSW process with full tool penetration was successfully performed, and the resulting metallurgical and mechanical properties are discussed in the following.

Orbital FSW was performed on API 5L X65 PSL2 high-strength low-alloy (HSLA) steel pipes with an inner clad layer (3 mm) of Inconel 625. Both pipe materials are metallurgically bonded. In other words, the bond between the materials is overall characterized by an interdiffusion. The base material (BM) was provided by Butting GmbH & Co., and the cladding process used on the pipes were carried out by hot-roll bonding16,17. The chemical composition of the API X65 PSL2 steel and Inconel 625 was determined by optical emission spectrometry (OES) and energy dispersive spectroscopy (EDS), respectively, and these results are given in Table 1.

The pipes had a total wall thickness of 9 mm and an external diameter of 310.5 mm. Single pass orbital FSW was performed on butt sections of the pipes with the pcBN tool of MegaStir™, designated as Q70, i.e., 70 wt% cBN and 30 wt% W–Re as the binder. The tool shows a convex radius shoulder with a diameter of 25 mm and a stepped spiral probe with a length of 8.5 mm.

A manipulator that is rigid enough to absorb the forces of the FSW process and apply the required torque to the pipes was developed to ensure a constant welding speed and guarantee proper clamping. A schematic drawing of the employed clamping system is shown in Fig. 1a. An internal clamping is required to prevent local collapse of the pipe during welding and guarantee the centering of the pipes and in this regard the quality of the weld. The external rollers support the force (Fz) applied by the FSW tool and avoid pipe deflection. The lateral clamping ensures full contact of the parallel cross-section of the two pipes to be welded. The rotatory union rotates the pipes at controlled rotational speed, determining the resultant welding speed, where the rotating FSW tool is kept at a fix spatial position. Figure 1b shows two sections of pipe set in the clamping system ready to be welded.

(a) Schematic drawing and (b) image of the clamping system developed for orbital friction stir welding.

The main features of the Hereon portal FSW system are rotational speed up to 6000 rpm, maximum axial force of 60 kN and maximum torque of 140 Nm. Argon shielding gas was used to protect the top surface of the weld around the pcBN tool from oxidation. During welding, the tool stays stationary, and the pipe rotates. When the pipe starts to rotate, the plasticized material is stirred around the rotating stationary tool producing the welded joint, i.e., the pipe movement is equivalent to the tool traverse speed in FSW of sheets.

An inherent feature of FSW is an exit hole left at the end of the process. Methods to avoid the exit hole, which could be considered as a substantial defect in pipes, are presented in the literature, including devices to eliminate14,18 or to fill it19. However, this aspect goes beyond the focus of this study and will therefore not be considered further. To demonstrate the capability of the employed clamping system in producing sound joints in clad pipes, two different process parameters were investigated in this study, selected based on previous work on X65 steel sheets clad by welding overlay with Inconel 6254. In this previous work, the force was varied between 60 and 40 kN, leading to good joints. Therefore, in this work, the intermediate value was chosen as the initial value (50 kN) and subsequently adopted to decrease by 10% to evaluate the corresponding response, see Table 2.

Microstructural analysis of the weld zones was carried out using Keyence VHX-6000 optical microscopy (OM) and an FEI Quant 650 FEG scanning electron microscopy (SEM) equipped with EDAX Apollo X EDS system and EDAX velocity EBSD camera. EDS was performed to analyze the chemical composition in the BM, starting on the steel side, passing through the interface zone, and ending on the Inconel side. In addition, EDS was used to evaluate the presence of M (C, N) carbonitrides and intermetallic compounds. Samples were prepared using standard metallography, followed by two-step etching. To reveal the microstructure of the X65 steel and alloy 625, a 2%-vol Nital and an Adler’s solution (25 ml H2O, 3 g CuCl2, 15 g FeCl3, 50 ml HCl) were used, respectively. For the electron backscatter diffraction (EBSD) analysis, after the standard metallography, samples were prepared with a frequency of 50 Hz for 1 h in the VibroMet 2 Vibratory Polisher machine. The EBSD investigation was performed using a step size of 0.25 μm, and the acquired data were analyzed using the TSL OIM 7.3 software. Struers DuraScan 70 was used to perform Vickers microhardness measurements in the cross-section using a load of 500 g (HV 0.5) with distances between indentations of 0.5 mm. The temperature was measured during FSW by a thermocouple (Type K) inserted in the tool shoulder through the locking collar. The thermocouple was held against the pcBN tool, allowing consistent temperature readings.

In the initial welding phase, i.e., during the initial plunging stage, the rotational speed was set to 750 rpm (Fig. 2a). As soon as the material around the probe is plasticized, the rotational speed is set to the target values, i.e., to 500 rpm and 400 rpm for Welds I and II, respectively, see Table 2. At this point, the pipe rotates at a welding speed of 2 mm/s. The process is force-controlled, with forces of 50 kN and 45 kN for Weld I and II, respectively. Since the process parameters in Weld II led to lower temperatures, Fig. 2b shows the higher material resistance from the machine response in terms of a slightly higher torque compared to Weld I. It is important to notice that the welds have different lengths, as Weld II had to be stopped prematurely after 327 s due an overheating in the machine. However, the welding length is more than sufficient for an in-depth analysis of the resulting properties.

(a) Rotational speed, axial force, and torque during the orbital FSW process for both pipes. (b) Tool temperature measured within the tool during the processes.

The microstructural features of the BM are shown in Fig. 3. The X65 steel is composed of acicular ferrite (AF), quasi-polygonal ferrite (QPF), polygonal ferrite (PF), carbides, and martensite/austenite (M/A) phase, while the CRA layer (Inconel 625) presents a microstructure of elongated austenitic grains and M(C, N) carbonitrides. In addition, carbides along grain boundaries can be observed, which are typically identified as M6C and M23C6 (Fig. 3a). Due to the hot roll-bonding process used to produce the clad pipes involving high deformation at elevated temperature, substitutional inter-diffusion of Ni and Cr to the steel side and Fe to the CRA side occurred, besides interstitial diffusion of C from steel to the CRA. That results in austenitic steel in the interface due to the stabilizing effect of Ni16,20. Figure 3b shows the EDS line scan along the interface of the pipe, presenting a clear transition from steel (Fe) to Inconel (Ni and Cr). Microhardness tests of the BM led to 210 HV, 249 HV, and 318 HV for steel, interface, and Inconel 625, respectively.

Microstructural analysis of the clad pipe BM, above the API X65 steel and below the interface of the Inconel 625; (b) EDS line scan utilized to identify the chemical composition along the steel/Inconel interface in the BM; (c,d) top surface appearance and macrostructure of Weld I and (e,f) top surface appearance and macrostructure of Weld II.

An overview of the two welded joints is also provided in Fig. 3. Weld I, Fig. 3c, resulted in a surface with more flash and a larger heat-affected zone (HAZ), Fig. 3d, when compared to that of the Weld II (Fig. 3e,f). Latter is expected due to the higher energy input, see Table 2, and the resulting higher temperature (Fig. 2b). The temperatures in the tool reached a maximum of 1020 °C for Weld I and 916.5 °C for Weld II.

The joint microstructure can be divided into three core regions: steel side, Ni-based alloy 625 side, and interface (Fig. 4a). On the steel side, the SZX65 and hard zone (HZX65) are observed. Similarly to other studies21,22,23, the HAZX65 can be subdivided into three sub-regions with different microstructures: the outer HAZ (OHAZX65), middle HAZ (MHAZX65), and the inner HAZ (IHAZX65). As observed in Fig. 2b, the X65 steel experienced a peak temperature above Ac3 (i.e., the critical temperature in the Fe–C diagram) during welding; the microstructure is transformed into the austenite, and according to the cooling rate and the peak temperature, the austenite is transformed to different microstructures in the form of martensite, bainite, ferrite, carbide or a combination of them22.

(a) Macrographs of different zones in the X65 steel side for Weld I and Weld II. (b) SZX65, (c) HZX65, (d) OHAZX65, (e) MHAZX65 and (f) IHAZX65. The yellow arrows point out the M/A phase. In the micrographs, the different zones analyzed on the Inconel side (g,h,i) are indicated already, see Fig. 5.

The SZX65, Fig. 4b, comprises AF and granular bainite. Additionally, since HZX65 may have experienced the highest deformation, peak temperatures, and cooling rates during FSW24, a lath bainite microstructure (LB) is observed (Fig. 4c). The OHAZX65, Fig. 4d shows a more refined equiaxed PF compared to the BMX65. In the MHAZX65, the resulting microstructure is of QPF, PF, and AF (Fig. 4e). The IHAZX65, Fig. 4f exhibits a mixed ferrite and bainite microstructure with finer prior austenite grain size and more PF than found in the SZX65. M/A phase pointed out in Fig. 5, was also found in both welds. With the aid of EBDS, it was possible to quantify the percentage of face-centered-cubic structure in the steel, and according to the measurements, the BM showed 0.2%, Weld I 0.5%, and Weld II 0.2% of M/A.

Optical micrographs of different zones in Inconel 625 for Weld I and Weld II: (a) SZ1625 showing refined austenitic grains, (b) SZ2625 shows characteristic coarser austenitic grains and (c) TMAZ625 deformed grains. SZ1625, SZ2625, and TMAZ625 are indicated in the macrographs of both welds as (g–i) in Fig. 5.

Figure 5 presents the microstructural zones on the Inconel 625. Two sub-regions can be identified in the SZ625, i.e., SZ1625 and SZ2625. The FSW process led to significant grain refinement in the bottom of SZ1625 (Fig. 5a). In SZ2625, coarser and equiaxial austenitic grains are found (Fig. 5b), which suggests that the material was exposed to higher thermal cycles in relation to SZ1625, causing grain growth. The TMAZ625 presents a deformed microstructure following the probe flow pattern (Fig. 5c). The cabonitrides found in the welds are the M (C, N), inherent of the BM, with a high amount of niobium, molybdenum, or titanium. Precipitate transformation was not found in the welds in an SEM investigation. According to the literature, carbide precipitation is unlikely to occur during FSW process, as prolonged exposure at elevated temperatures seem to be required5,20,25.

Figure 6a–c shows the grain boundary misorientation (GBM) and average grain boundary area (GB) distribution maps of the BM and SZs for Welds I and II for the X65 steel, in which the green lines represent very high-angle grain boundaries, i.e. grain boundary misorientation ≥ 45°, the red lines represent grain boundary misorientation between 15° and 45° and the black lines represent low-angle grain boundaries (LAGBs), i.e. < 15°. The steel SZX65 showed around 51% of LAGBs and the BM reached 30% of LAGBs, indicating that a high number of dislocations were created in the SZX65. The high amount of LABs found within the SZX65 (~ 51%) and small peaks above 45° (~ 32%) suggests that the microstructure here has less acicular ferrite but more bainite22,26. The average GB area increased with the energy input, i.e. from 8.6 µm2 in the BM to 17.2 µm2 in Weld II and 29.2 µm2 in Weld I, see Fig. 6a–c.

Grain boundary misorientation analysis via EBSD: (a–c) steel side and (d,e) Inconel 625 side; (a,d) BM; (b) SZX65 and (e) SZ625 of Weld I and (c) SZX65 and (f) SZ625 of Weld II.

It is important to point out that the recrystallization mechanism for austenite and ferrite phases occurs differently because of their distinct stacking fault energy (SFE)27. Ferrite has a high SFE and immediately underwent the recovery process; therefore, sub-grains were formed during hot deformation. Hence, a great number of LABs were generated within the grains. However, phases with low SFE, such as the austenite, can easily form recrystallization nuclei28,29,30. In Fig. 6d–f, the black line represents the HAGBs (≥ 15°), and the green line LAGBs (< 15°) for Inconel 625. The maps show that the concentration of HAGBs increases from the BM (64.8%) to the SZ625 (around 93.0%), indicating a fully recrystallized state. In addition, due to the inherent characteristics of FSW, such as severe plastic deformation, high strain rates, enough heat input, and fast cooling rate, thus an effective grain refinement is observed, from an average GB area of 15.4 µm2 in the BM to 2.5 µm2 and 1.9 µm2 in the SZ1625 of Weld I and Weld II, respectively.

The interface of the welds is detailed in Fig. 7. At the joining temperature during FSW, as Inconel 625 and API X65 steel have the same crystal structure (fcc), similar melting points, and comparable flow stresses31, these characteristics allow the alloy 625 to flow around the probe and to drain into the steel, forming alternating bands of materials in the SZ, which is consistent with findings from Rodriguez & Ramirez2. This is also in agreement with other studies on dissimilar FSW welds32. For both welds, as can be seen in Fig. 7a,b,e,f, Inconel 625 hooks were formed in API X65 steel. The height of the hooks is around 1.38 mm (0.86 mm) on the AS and 0.84 mm (1.71 mm) on the RS for Weld I (Weld II). The shape of the alternating bands, might be related to the process parameters and heat input achieved. A higher heat input seems to contribute to a more homogeneous mixture of the materials. Figure 7c,d show EDS images, indicating Fe, and Ni rich regions. In Fig. 7g,h detailed images of the SZ are shown.

Different features in the interface of the clad pipes welded by FSW: SZ of Weld I (a) and of Weld II (b); EDS chemical composition of Weld I SZ (c) and Weld II (d), where green indicates Fe and red Ni; hook on AS of Weld I (e) and Weld II (f); detail of the alternated bands of Fe–Ni in the SZ in Weld I (g,h); EBSD analysis of interface in BM (i), Weld I (k) and Weld II (m); Identification of bcc (green) and fcc (red) structures of corresponding EBSD micrographs is shown for the interface of BM (j), Weld I (l) and Weld II (n).

Results of EBSD analysis at the interface of the BM are shown in Fig. 7i and for Weld I, and Weld II in Fig. 7k,m, respectively. The corresponding separation into fcc (austenite) and bcc (ferrite) structures is presented in Fig. 7j,l,n. In the interface, the BM steel has a GB area of 10.9 µm2, and the clad bonding line is clearly observed. Weld I and Weld II present grain growth with an average GB area of 18.7 µm2 and 14.18 µm2, respectively. It is interesting to notice that the grain growth in the X65 steel in the mixed interface is smaller than in the SZX65 (29.2 µm2 and 17.7 µm2, for the welds I and II, respectively). After the FSW process, the line of the clad bonding cannot be easily distinguished anymore. The Inconel 625 grains in the mixed interface region underwent recrystallization and Weld I, with higher energy input showed an average grain size of 12.1 µm2 and Weld II, with lower energy input, an average grain size of 8.88 µm2. In both cases, the average grain size observed in the mixed interface presented a significant grain growth compared to the SZ1625 (~ 2.0 µm2).

Vickers microhardness for Weld I and Weld II show differences in all zones of the Inconel 625 (Fig. 8). In the BM625 near the weld, values ranged between 310 and 360 HV for Weld I and Weld II, respectively. On the RS, where relatively coarse recrystallized Inconel 625 grains were found in SZ2625, the maximum values were 284 HV and 330 HV for Weld I and Weld II, respectively. The hardness values in the interface SZ are significantly lower due to the mixing between Inconel 625 and X65 steel, i.e., for Weld I, the values ranged from 218 to 303 HV, and for Weld II, even between 187 and 344 HV. The complex banded patterns, see Fig. 7a–d, contributed to the high hardness variations, as the BMs (X65 steel and Inconel 625) have different metallurgical and mechanical properties. On the steel side, the minimum hardness is found in the HAZX65, varying between 172 and 180 HV, which agrees with results in the literature14,24. The hardness increases slightly with decreasing energy input while the width of the HAZX65 decreases comparing the two welds. A small increase in microhardness was noted within the SZX65, ranging between 200 and 250 HV for both welds. This slight improvement in microhardness in the SZX65 is expected due to the severe deformation at elevated temperatures and high cooling rate, resulting in a more significant amount of bainite in the steel21,33. In the SZ X65, higher strain rates and associated plastic deformation caused higher hardness zones on the AS compared to the RS. The BM in the interface region showed a microhardness of 245 HV.

Microhardness maps of Weld I and Weld II, created via Origin, Version 2021. OriginLab Corporation, Northampton, MA, USA. Available: https://www.originlab.com/.

The feasibility of orbital friction stir welding (FSW) for joining X65 carbon steel clad pipes with Inconel 625 was presented in this work. The results can be briefly summarized as follows:

The developed system was proven to produce FSW joints in one pass with full penetration and without volumetric defects. Friction-stir welded clad pipes of a total 9 mm wall thickness of API X65 steel and alloy 625 were produced at axial forces of 45–50 kN, tool rotational speeds of 400–500 rpm and a welding speed of 2 mm/s.

The orbital FSW process altered the microstructure of the base material. In API X65 PSL2 steel, three sub-regions were observed in the heat-affected zone with mainly ferrite microstructure. The predominant microstructures in the stir zone and hard zone, were bainite and acicular ferrite. In Inconel 625, two different regions were identified within the stir zone, one associated with refined recrystallized grains and higher hardness and other with grain growth and lower hardness. Weld II showed the same percentage of M/A as the base material, i.e., 0.2% and Weld I showed an increase of M/A to 0.5%.

Alternating bands of materials were found in the stir zone, following the tool flow pattern. A higher energy input seems to contribute to a homogeneous mixture of materials in the stir zone. In addition, higher energy input led to lower hardness and larger heat affected zones.

The grain size of Inconel 625 varied along the stir zone. The concentration of high-angle grain boundaries increased from the base material (64.8%) to the stir zone (~ 93.0%), indicating that full recrystallization occurred in the Inconel 625. In the X65 steel, there was also a variation in the grain size, with a more remarkable grain growth in the SZx65 compared to the X65 steel in the mixed interface. The high amount of grain boundaries with misorientation lower than 15° in the stir zone (~ 51%) and fewer peaks above 45° (~ 32%) suggest an increase in the amount of the bainite microstructure after FSW.

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

A Correction to this paper has been published: https://doi.org/10.1038/s41598-023-39136-z

Landell, R. M. et al. Investigation of friction stir welding process applied to ASTM 572 steel plate cladded with Inconel®625. Weld. World 65(3), 393–403. https://doi.org/10.1007/s40194-020-01007-w (2021).

Article CAS Google Scholar

Rodriguez, J. & Ramirez, A. J. Microstructural characterisation of friction stir welding joints of mild steel to Ni-based alloy 625. Mater. Char. 110, 126–135. https://doi.org/10.1016/j.matchar.2015.10.023 (2015).

Article CAS Google Scholar

Ramirez, A. J., et al. Friction stir welding of steels for the oil and gas industry. https://doi.org/10.1533/9781782421641.75 (2013).

de Lima Lessa, C. R. et al. Two-pass friction stir welding of cladded API X65. Proc. Manuf. 1, 1010–1015. https://doi.org/10.1016/j.promfg.2020.04.311 (2020).

Article Google Scholar

Bossle, E. P. et al. Friction stir lap welding of Inconel 625 and a high strength steel. Metals (Basel) 13(1), 1. https://doi.org/10.3390/met13010146 (2023).

Article CAS Google Scholar

Mishra, R. S. & Ma, Z. Y. Friction stir welding and processing. Mater. Sci. Eng. R. Rep. 50(1–2), 1–78. https://doi.org/10.1016/j.mser.2005.07.001 (2005).

Article CAS Google Scholar

Thomas, W., Nicholas, E. D., Needham, J. C., Murch, M. G., Templesmith, P., & Dawes, C.J. Friction stir welding. PCT/GB92102203 (1991).

Senthil, S. M., Bhuvanesh Kumar, M. & Dennison, M. S. A contemporary review on friction stir welding of circular pipe joints and the influence of fixtures on this process. Genet. Res. https://doi.org/10.1155/2022/1311292 (2022).

Article Google Scholar

Gibson, B. T. et al. Friction stir welding: Process, automation, and control. J. Manuf. Process 16(1), 56–73. https://doi.org/10.1016/j.jmapro.2013.04.002 (2014).

Article Google Scholar

Liu, F. C., Hovanski, Y., Miles, M. P., Sorensen, C. D. & Nelson, T. W. A review of friction stir welding of steels: Tool, material flow, microstructure, and properties. J. Mater. Sci. Technol. 34(1), 39–57. https://doi.org/10.1016/j.jmst.2017.10.024 (2018).

Article CAS Google Scholar

Venkatesh, K. M., Arivarsu, M., Manikandan, M. & Arivazhagan, N. Review on friction stir welding of steels. Mater. Today Proc. 5(5), 13227–13235. https://doi.org/10.1016/j.matpr.2018.02.313 (2018).

Article CAS Google Scholar

Marré, M., Ruhstorfer, M., Tekkaya, A. E. & Zaeh, M. F. Manufacturing of lightweight frame structures by innovative joining by forming processes. Int. J. Mater. Form. 2(SUPPL. 1), 307–310. https://doi.org/10.1007/s12289-009-0524-7 (2009).

Article Google Scholar

Chen, B. X., Chen, K., Liang, Z. Y., Yao, J. S., Zhang, L. T., & Shan, A. D. Friction stir welding of aluminum alloy and copper dissimilar pipes of thin wall and small diameter. https://doi.org/10.1533/9781782421641.249 (2013).

Feng, Z., Steel, R., Packer, S., & David, S. A. Friction stir welding of API Garde 65 steel pipes. In Volume 6: Materials and Fabrication, Parts A and B, ASMEDC, pp. 775–779. https://doi.org/10.1115/PVP2009-77248 (2009).

Giorjão, R. A. R. et al. Microstructure and mechanical properties of friction stir welded 8 mm pipe SAF 2507 super duplex stainless steel. J. Market. Res. 8(1), 243–249. https://doi.org/10.1016/j.jmrt.2018.01.002 (2019).

Article CAS Google Scholar

Giudice, F., Missori, S., Murdolo, F. & Sili, A. Metallurgical characterization of the interfaces in steel plates clad with austenitic steel or high Ni alloys by hot rolling. Metals (Basel) 10(2), 1. https://doi.org/10.3390/met10020286 (2020).

Article CAS Google Scholar

Reichel, T., Beissel, J., Krämer, E., Pavlyk, V., & Heigl, G. Production of metallurgically cladded pipes for high end applications in the oil and gas industry (2008). [Online]. Available: http://www.asme.org

Hattingh, D. G. et al. Semiautomatic friction stir welding of 38 mm OD 6082–T6 aluminium tubes. J. Mater. Process. Technol. 238, 255–266. https://doi.org/10.1016/j.jmatprotec.2016.07.027 (2016).

Article CAS Google Scholar

Ghavimi, A. H., Aboutalebi, M. R. & Seyedein, S. H. Exit-hole repairing in friction stir welding of AA5456 pipe using consumable pin. Mater. Manuf. Processes 35(11), 1240–1250. https://doi.org/10.1080/10426914.2020.1772491 (2020).

Article CAS Google Scholar

DuPont J.N., Lippold J.C., & Kiser S.D. Welding metallurgy and weldability of nickel-base alloys (2009).

Barnes, S. J. et al. Friction stir welding in HSLA-65 steel: Part I. Influence of weld speed and tool material on microstructural development. Metall. Mater. Trans. A Phys. Metall. Mater. Sci. 43(7), 2342–2355. https://doi.org/10.1007/s11661-012-1110-z (2012).

Article ADS CAS Google Scholar

Xie, G. M. et al. Microstructure and mechanical properties of X80 pipeline steel joints by friction stir welding under various cooling conditions. Acta Metall. Sin. (English Letters) 33(1), 88–102. https://doi.org/10.1007/s40195-019-00940-0 (2020).

Article CAS Google Scholar

Avila, J. A., Lucon, E., Sowards, J., Mei, P. R. & Ramirez, A. J. Assessment of ductile-to-brittle transition behavior of localized microstructural regions in a friction-stir welded X80 pipeline steel with miniaturized charpy V-Notch testing. Metall. Mater. Trans. A Phys. Metall. Mater. Sci. 47(6), 2855–2865. https://doi.org/10.1007/s11661-016-3473-z (2016).

Article ADS CAS Google Scholar

Aydin, H. & Nelson, T. W. Microstructure and mechanical properties of hard zone in friction stir welded X80 pipeline steel relative to different heat input. Mater. Sci. Eng., A 586, 313–322. https://doi.org/10.1016/j.msea.2013.07.090 (2013).

Article CAS Google Scholar

Shankar, V., Bhanu, K., Rao, S., & Mannan, S. L. Microstructure and mechanical properties of Inconel 625 superalloy [Online]. Available: www.elsevier.nl/locate/jnucmat.

Shrestha, S. L. et al. An automated method of quantifying ferrite microstructures using electron backscatter diffraction (EBSD) data. Ultramicroscopy 137, 40–47. https://doi.org/10.1016/j.ultramic.2013.11.003 (2014).

Article CAS PubMed Google Scholar

Sharamanian, M., Kangazian, J. & Szpunar, J. A. Insights into the microstructure evolution and crystallographic texture of API X-65 steel/UNS S32750 stainless steel dissimilar welds by EBSD analysis. Weld. World 65, 973–986. https://doi.org/10.1007/s40194-020-01062-3 (2021).

Article CAS Google Scholar

Song, K. H., Fujii, H. & Nakata, K. Effect of welding speed on microstructural and mechanical properties of friction stir welded Inconel 600. Mater. Des. 30(10), 3972–3978. https://doi.org/10.1016/j.matdes.2009.05.033 (2009).

Article CAS Google Scholar

Ahmed, M. M. Z., Wynne, B. P. & Martin, J. P. Effect of friction stir welding speed on mechanical properties and microstructure of nickel based super alloy Inconel 718. Sci. Technol. Weld. Joining 18(8), 680–687. https://doi.org/10.1179/1362171813Y.0000000156 (2013).

Article CAS Google Scholar

Das, H., Mondal, M., Hong, S. T., Lee, J. W. & Cho, H. H. Texture and precipitation behavior of friction stir welded Inconel 825 alloy. Mater. Today Commun. 25, 1. https://doi.org/10.1016/j.mtcomm.2020.101295 (2020).

Article CAS Google Scholar

Jin, H., Ayer, R., Mueller, R., Ling, S. & Ford, S. Metallography of dissimilar Fe-Ni joint by friction stir welding. Int. J. Offshore Polar Eng. 16(03), 1 (2006).

CAS Google Scholar

Murr, L. E. A review of FSW research on dissimilar metal and alloy systems. J. Mater. Eng. Perform 19(8), 1071–1089. https://doi.org/10.1007/s11665-010-9598-0 (2010).

Article CAS Google Scholar

Wei, L. & Nelson, T. W. Influence of heat input on post weld microstructure and mechanical properties of friction stir welded HSLA-65 steel. Mater. Sci. Eng., A 556, 51–59. https://doi.org/10.1016/j.msea.2012.06.057 (2012).

Article CAS Google Scholar

Download references

This work was conducted during a scholarship supported by Leuphana Universität Lüneburg (Carla Volff Amavisca), which is gratefully acknowledged. Financial support from DAAD via funds of the Federal Ministry of Education and Research (BMBF) under project number 57598245 is gratefully acknowledged. Financed by Capes—Brazilian Federal Agency for Support and Evaluation of Graduate Education within the Ministry of Education of Brazil (Fabiano Dornelles Ramos) is gratefully acknowledged. We also would like to thank MSc. Camila Caroline Castro for her helpful support on acquiring the EBDS images for this work.

Open Access funding enabled and organized by Projekt DEAL. This publication was funded by the German Research Foundation (DFG).

Institute for Production Technology and Systems, Leuphana University Lüneburg, Leuphana University Lüneburg, Universitätsallee 1, 21335, Lüneburg, Germany

C. V. Amavisca & B. Klusemann

Federal University of Rio Grande do Sul (UFRGS), Av. Paulo Gama, 110, Porto Alegre, 90040-060, Brazil

C. V. Amavisca, J. G. Schroeder & A. Reguly

Institute of Materials Mechanics, Solid State Materials Processing, Helmholtz-Zentrum Hereon, Max-Plank-Straße 1, 21502, Geesthacht, Germany

C. V. Amavisca, L. Bergmann, C. R. de L. Lessa, J. G. Schroeder, F. D. Ramos & B. Klusemann

Federal Institute of Rio Grande do Sul (IFRS), R. Avelino Antônio de Souza 1730, Caxias do Sul, 95043-700, Brazil

C. R. de L. Lessa & F. D. Ramos

Federal University of Santa Maria (UFSM), Rod. Taufik Germano, 3013, Cachoeira do Sul, 96503-205, Brazil

G. V. B. Lemos

You can also search for this author in PubMed Google Scholar

C.V.A.: conceptualization, methodology, data curation, investigation, formal analysis, writing, and editing original draft; L.B.: friction stir welding, investigation, review, and editing; C.R.L.L.: friction stir welding and investigation; J.G.S.: friction stir welding and investigation; F.D.R.: investigation, review, and editing; G.V.B.L.: investigation, writing, review, and editing; A.R.: supervision and review; B.K: conceptualization, supervision, writing, review, and editing.

Correspondence to C. V. Amavisca.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

The original online version of this Article was revised: The Funding section in the original version of this Article was incomplete. Full information regarding the corrections made can be found in the correction for this Article.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Amavisca, C.V., Bergmann, L., Lessa, C.R.d.L. et al. Feasibility of orbital friction stir welding on clad pipes of API X65 steel and Inconel 625. Sci Rep 13, 10669 (2023). https://doi.org/10.1038/s41598-023-37913-4

Download citation

Received: 06 April 2023

Accepted: 29 June 2023

Published: 01 July 2023

DOI: https://doi.org/10.1038/s41598-023-37913-4

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.